• română
    • English
    • français
    • Deutsch
    • español
    • italiano
  • română 
    • română
    • English
    • français
    • Deutsch
    • español
    • italiano
  • Logare
Vezi articolul 
  •   Pagina principală
  • Scientific papers - Annals of "Dunarea de Jos" University of Galati - Analele științifice ale Universității "Dunărea de Jos" din Galați
  • Fascicula IX
  • 1993 -2018
  • 2005 fascicula9 nr1
  • Vezi articolul
  •   Pagina principală
  • Scientific papers - Annals of "Dunarea de Jos" University of Galati - Analele științifice ale Universității "Dunărea de Jos" din Galați
  • Fascicula IX
  • 1993 -2018
  • 2005 fascicula9 nr1
  • Vezi articolul
JavaScript is disabled for your browser. Some features of this site may not work without it.

Behavior of 1% Cr Steels at Fluidized Bed Nitrocarburizing

Thumbnail
View/Open
ugal_f9_nr1_2005_16_Dobrovici.pdf (578.2Kb)
Dată
2005
Autor
Dobrovici, Sorin
Cazacu, Nelu
Bâclea, Adolf
Drugescu, Elena
Metadata
Arată înregistrarea completă a articolului
Abstract
Paper is based by nitrocarburizing experiments made on pilot installation. For experiments were used different samples of steel at different nitrocarburizing regimes. Influence factors were: temperature and ammonia concentration. Treatment time had a constant value 2h30min. Influences of factors were investigated by: samples mass modifications, surface structure (micrograph), layer depth to all samples and hardness HV5 on the surface. The results confirm possibility to use fluidized med like nitrocarburizing media and good behavior of steel.
URI
http://10.11.10.50/xmlui/handle/123456789/5458
Colecții
  • 2005 fascicula9 nr1 [18]

DSpace 6.0 | Copyright © Arthra Institutional Repository
Contactați-ne | Trimite feedback
Theme by 
Atmire NV
 

 

Răsfoiește

În tot DSpaceComunități; ColecțiiDupă data publicăriiAutoriTitluriSubiecteAceastă colecțieDupă data publicăriiAutoriTitluriSubiecte

Contul meu

Conectare

DSpace 6.0 | Copyright © Arthra Institutional Repository
Contactați-ne | Trimite feedback
Theme by 
Atmire NV